Carbon/Graphite filled PTFE materials have better wear resistance than carbon filled PTFE materials. Carbon/Graphite filled PTFE materials have excellent extrusion resistance and good wear resistance and will work well in both lubricated and non-lubricated environments.
Carbon/Graphite filled PTFE materials are used in static and dynamic applications and used against chromium-plated surface and steel.
PBY Material Codes:
PB10105G - 23% Carbon 2% Graphite Filled PTFE
Excellent for dry and poorly lubricated environments
Improved thermal and electrical conductivity vs Virgin PTFE
Reduced deformation under load compared to virgin PTFE
This product meets ASTM D4745 Type I Grade 8 and AMS 3678/7 requirements.
Property | Test Method | Units | Typical Value |
---|---|---|---|
Color | - | - | Black |
Specific Gravity | ASTM D792 | - | 1.95 - 2.150 |
Hardness Shore D | ASTM D2240 | - | 65 - 75 |
Tensile Strength, min. | ASTM D4745 | PSI [MPa] | 1,400 [9.6] |
Elongation at Break, min. | ASTM D4745 | % | 20 |
Second Melt Peak Temp. | ASTM D3418 | °F [°C] | 621 [327] |
Glass Transition Temp. | ASTM D3418 | °F [°C] | -143 [-97]; 246 [119] |
2571 E. Lindsay Privado, Ontario, CA 91761 USA
Phone (909) 930-6700 | Fax (909) 930-6702
Email: This email address is being protected from spambots. You need JavaScript enabled to view it.
via U.Foscolo, 2/4
20060 Basiano, Milano
ITALY
Tel.: +39 0295760331
Fax: +39 0295760333
This email address is being protected from spambots. You need JavaScript enabled to view it.
13522 Manhasset Rd
Apple Valley (CA) 92308
USA
Tel: +1 7602404999
This email address is being protected from spambots. You need JavaScript enabled to view it.
www.polymerconcepts.com